Ntho | Ho hlokahala | Boleng ba teko | |
Alumina ceramic | Litaba tsa Al2O3 | 92% | 92.09% |
Botenya | >3.60g/cm3 | 3.62g/cm3 | |
Rockwell Hardness | > 85HRA | 90HRA | |
Rabara | Matla a tšepe | =14Mpa | 14Mpa |
Ho lelefatsa ha ho hloleha | 450% | 450% | |
Bothata ba lebopo | 60+/-5 Lebopo A | 60+/-5 Lebopo A | |
Sekhahla sa deformation sa tensile | <=24% | 30% | |
Abradability | 0.0005g (P=74N,n=800rpm,t=30min,Quartz snad) | 0.0005g (P=74N,n=800rpm,t=30min,Quartz snad) | |
Khatello ea ho kuta | 12Mpa | 12Mpa | |
Botenya ba ceramic | 7mm | 7mm | |
Botenya ba rabara | 5mm | 5mm |
1: Haeba rolara e se e tsofetse, pele ho ts'ebetso, o hloka ho tlosa sekhomaretsi hana, ka kopo sebelisa grinder ea angle le poleiti ea tšepe ea tungsten ho bentša bokaholimo ba rolara, botenya ba bokaholimo bakeng sa kalafo ea polish ke 30um.
2. Hlatsoa sesepa holim'a sefahleho se betliloeng sa rolara, hloekisa litšila le litšila tsa mafura.
3. Emela hore sesepa se omme, borashe boalo ba tšepe holim'a rolara ho qoba ho bola ho tsoa linthong tse kantle.
4. Kopanya sekhomaretsi sa sekhomaretsi sa SK313, ebe u borashe sekhomaretsi holim'a rolara, ka mor'a ho fola, garasa sekhomaretsi sa SK313 holim'a rolara hape, u sa ntse u le joalo brush SK313 mokokotlong o moputsoa oa rabara ea ceramic liner.
5. Ha sekhomaretsi se khomarela hanyenyane bakeng sa monoana, ka kopo, beha lesela la rabara ka holim'a rolara, 'me u sebelise hamore ea rabara e otla motsoako ka thata, qetellong beha moemeli oa ho lokisa rabara sebakeng sa motsoako oa li-rabara tsa ceramic liner. bakeng sa ho tiisa kalafo.